Plain specimens of two batches of the commercial spring steel BS 251A58 of nominally
identical processing but significantly differing levels of non-metallic inclusion levels,
have been tested in rotating bending.
The data produced has been analysed against some recent methods for the prediction of
fatigue properties in high strength materials containing defects.
The materials tested were specifically selected for their disparate cleanliness levels,
yielding specimens with differing inclusion distribution and maxima. The morphology
of critical inclusions is identical between the two material batches. Material
microstructure is tempered martensite with ultimate tensile strength of approximately
2000 MPa, which renders it well above the strength level where sensitivity to defects
causes variability in fatigue behaviour.
Models have been selected from the literature for the prediction of fatigue limit using
characterisation of the local microstructural state and the size and critical position of
non-metallic inclusions. These models have been validated by the analysis of specific
failures after fractographic analysis. It has been shown that these models are acceptably
accurate and generally conservative.
Difficulties in experimental work have precluded the planned measurement of crack
growth rates during the current test work. These difficulties have yielded a
superimposed mean stress to the rotating bend test. This mean stress has been quantified
for each test and the result coupled with a parameter for mean stress correction. The
validity of the mean stress correction has been proven in this work to be valid. More
consistent results are observed for the mean stress corrected data.
A statistical method for the prediction of maximum non-metallic inclusion size for a
given number of specimens or components from small sample microsection analyses
has yielded good results when compared to the fractographic observations. This work
has investigated the effect of varying magnification level and number of fields surveyed
on the accuracy of prediction and recommendations are made for the method for
obtaining best accuracy.
A 'unified' crack propagation life model from the literature has been applied which
combines long and short crack growth regimes. The model has shown good correlation
to the current data but only after fitting of constants and only within the low cycle
regime. Relationships presented in the literature between constants and the material
ultimate tensile strength were found to be inapplicable to the current material at this
strength level.
Date of Award | 2001 |
---|